kevlar- A high performance fiber (P-1)

Kevlar is the registered trademark for a para-aramid synthetic fiber, related to other aramids such as Nomex and Technora. Kevlar has many applications, ranging from bicycle tires and racing sails to body armor, because of its high tensile strength-to-weight ratio; by this measure it is 5 times stronger than steel. It is also used to make modern drumheads that withstand high impact. When used as a woven material, it is suitable for mooring lines and other underwater applications.
Production
A similar fiber called Twaron with roughly the same chemical structure was developed by Akzo in the 1970s; commercial production started in 1986, and Twaron is now manufactured by Teijin.Kevlar is synthesized in solution from the monomers 1,4-phenylene-diamine (para-phenylenediamine) and terephthaloyl chloride in a condensation reaction yielding hydrochloric acid as a byproduct. The result has liquid-crystalline behavior, and mechanical drawing orients the polymer chains in the fiber's direction. Hexamethylphosphoramide (HMPA) was the solvent initially used for the polymerization, but for safety reasons, DuPont replaced it by a solution of N-methyl-pyrrolidone and calcium chloride. As this process had been patented by Akzo (see above) in the production of Twaron, a patent war ensued.Kevlar (poly paraphenylene terephthalamide) production is expensive because of the difficulties arising from using concentrated sulfuric acid, needed to keep the water-insoluble polymer in solution during its synthesis and spinning.

Kevlar K-29 – in industrial applications, such as cables, asbestos replacement, brake linings, and body/vehicle armor.
Kevlar K49 – high modulus used in cable and rope products.
Kevlar K100 – colored version of Kevlar
Kevlar K119 – higher-elongation, flexible and more fatigue resistant
Kevlar K129 – higher tenacity for ballistic applications
Kevlar AP – 15% higher tensile strength than K-29[10]
Kevlar XP – lighter weight resin and KM2 plus fiber combination[11]
Kevlar KM2 – enhanced ballistic resistance for armor applications[12]